標題: 鐵硒類超導體FeSexTe1-x物理性質之研究
Physical Properties of FeSexTe1-x superconducting system
作者: 胡任宥
Hu, Ren-You
關鍵字: superconductivity
鐵硒
超導
出版社: 奈米科學研究所
引用: 1. Maw-Kuen Wu, July 28, 2008,Superconductivity in the PbO- type structure α-FeSe.,PNAS September 23,2008,vol.105, no.38 . 2. Kuo-Wei Yeh,Tzu-Wen Huang,Yi-lin Huang,Ta-Kun Chen, Fong- Chi Hsu,Phillip M.Wu,Yong-Chi Lee,Yan-Yi Chu,Chi-Lian Chen,Jiu-Yong Luo,Der-Chung Yan and Maw-Kuen Wu,EPL, 84 (2008) 37002 . 3. Kazumasa HORIGANE, Haruhiro HIRAKA, and Kenji OHOYAMA, Relationship between Structure and Superconductivity in FeSe1-xTex,Journal of the Physical Society of Japan Vol. 78, No. 7, July, 2009, 074718 . 4. B. C. Sales, A. S. Sefat, M. A. McGuire, R. Y. Jin, and D. Mandrus Oak Ridge National Laboratory, Oak Ridge, Tennessee 37831, USA,Bulk superconductivity at 14 K in single crystals of Fe1+yTexSe1−x,PHYSICAL REVIEW B 79, 094521,2009 . 5. 吳茂昆院士(物理研究所),鐵基(Iron-based)超導體的發展, 中央研究院週報第1200期 6. 呂台華、吳景淼、洪姮娥等編著,超導體簡介,台灣書店(1998) 7. 譯者:曾煥華,審定者:林雲海,超導體的世界,銀禾文化(1989) 8. 鄭人瑞著,金屬超導體Y1-XSmXNi2B2C及Y1-XSmXPd5B3C0.4物理性 質之研究,國立中興大學物理研究所碩士論文(2002) 9. OXFORD INSTRUMENTS, optistatAC-V PT Cooler operator’s Handbook.
摘要: 鐵硒超導材料是近年來熱門的研究對象,本實驗是利用固態反應法成功的製作超導材料FeSe1-xTex(x=0、0.4、0.6、0.7、0.75、0.8、0.85), X-ray的晶格繞射圖形發現某些角度的峰值,隨著Te的摻雜比例愈高而有偏移的現象,計算結果a軸與c軸都有增長的趨勢,但透過電性與磁性的量測結果,超導轉變溫度(Tc)與c軸並沒有成比例的關係,相較鐵基類的超導體c軸(鐵層間距)愈長Tc愈高,而有所差異,本實驗研究結果為Te含量愈接近0.6,則電阻率的量測及磁性的M-T關係作圖,其超導性都是最佳的。
URI: http://hdl.handle.net/11455/17295
其他識別: U0005-1108201015033600
文章連結: http://www.airitilibrary.com/Publication/alDetailedMesh1?DocID=U0005-1108201015033600
Appears in Collections:奈米科學研究所

文件中的檔案:

取得全文請前往華藝線上圖書館



Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.