標題: 以立體障礙控制合成含一級胺官能基Benzoxazine單體與新穎材料Poly(benzoxazine imide)之製備及性質探討
Steric hindrance-control synthesis of primary amine-containing benzoxazines, and properties of the resulting poly(benzoxazine imide) thermosets.
作者: 汪孟緯
Wang, Meng-Wei
關鍵字: 氧代氮代苯并環己烷
benzoxazine
立體障礙
一級胺
primary amine
steric hindrance
出版社: 化學工程學系所
引用: 1. Chernykh, A.; Agag, T.; Ishida, H. Macromolecules 2009, 42, 5121. 2. Liu, Y.-L.; Chou, C.-I. J. Polym. Sci. Part A: Polym. Chem. 2005, 43, 5267. 3. Agag, T.; Takeichi, T. Macromolecules 2001, 34, 7257. 4. Jin, L.; Agag, T.; Yagci, Y.; Ishida, H. Macromolecules 2011, 44, 767. 5. Oie, H.; Mori, A.; Sudo, A.; Endo, T. J. Polym. Sci. Part A: Polym. Chem. 2012, 50, 4756. 6. Liu, Y.-L.; Yu, J.-M. J. Polym. Sci. Part A: Polym. Chem. 2006, 44, 1890. 7. Andreu, R.; Reina, J. A.; Ronda, J. C. J. Polym. Sci. Part A: Polym. Chem. 2008, 46, 6091. 8. Agag, T.; Arza, C. R.; Maurer, F. H. J.; Ishida, H. Macromolecules 2010, 43, 2748. 9. Ning, X.; Ishida, H. J. Polym. Sci. Part A: Polym. Chem. 1994, 32, 1121. 10. Wang, C.-F.; Su, Y.-C.; Kuo, S.-W.; Huang, C.-F.; Sheen, Y.-C.; Chang, F.-C. Angew. Chem. Int. Ed. 2006, 45, 2248. 11. Kiskan, B.; Yagci, Y.; Ishida, H. J. Polym. Sci. Part A: Polym. Chem. 2008, 46, 414. 12. Tuzun, A.; Kiskan, B.; Alemdar, N.; Erciyes, A. T.; Yagci, Y. J. Polym. Sci. Part A: Polym. Chem.2010, 48, 4279. 13. Baqar, M.; Agag, T.; Ishida, H.; Qutubuddin, S. Polymer 2011, 52, 307. 14. Takeichi, T.; Guo, Y.; Agag, T. J. Polym. Sci. Part A: Polym. Chem. 2000, 38, 4165. 15. Agag, T.; Arza, C. R.; Maurer, F. H. J.; Ishida, H. Polym. Chem. 2011, 49, 4335. 16. Agag, T.; Arza, C. R.; Maurer, F. H. J.; Ishida, H. Macromolecules 2010, 43, 2748. 17. Holly, F. W.; Cope, C. J. Am. Chem. Soc. 1944, 66, 1875. 18. Burke, W. J. J. Am. Chem. Soc.1949, 71, 609. 19. Russell, V. M.; Koenig, J. L.; Low, H.-Y.; Ishida, H. J. Appl. Polym. Sci. 1998, 70, 1413. 20. Brunovska, Z.; Liu, J.-P.; Ishida, H. Macromol. Chem. Phys.1999, 200, 1745. 21. Lin, C.-H.; Chang, S.-L.; Hsieh, C.-W. Polymer 2008, 49, 1220. 22. Takeichi, T.; Kano, T.; Agag, T. Polymer 2005, 46, 12172. 23. Lin, C.-H.; Chang, S.-L.; Shen, T.-Y.; Shih, Y.-S.; Lin, H.-T.; Wang, C.-F. Polym. Chem. 2012, 3, 935. 24. Nagai, A.; Kamei, Y.; Wang, X.-S.; Omura, M.; Sudo, A.; Nishida, H.; Kawamoto, E.; Endo, T. J. Polym. Sci. Part A: Polym. Chem. 2008, 46, 2316. 25. Duffy, J. V.; Lee, G. F. J. Appl. Polym. Sci. 1988, 35, 1367. 26. Grenier-Loustalot, M.-F.; Cunha, L. D. Polymer 1998, 39, 1799. 27. Lin, C.-H.; Chang, S.-L.; Peng, L.-A.; Peng, S.-P.; Chuang, Y.-H. Polymer 2010, 51, 3899. 28. Sarojadevi, M.; Hariharan, R.; Amutha, N. Polyimides and Other High-Temperature Polymers: Synthesis, Characterization and Application 2009, 5, 43. 29. Li, Y.-S.; Wang, X.-Q.; Ding, M.-X.; Xu, J.-P. J. Appl. Polym. Sci. 1996, 61, 741. 30. Yoda, N.; Hiramoto, H. J. Macromol. Sci. Shem. 1984, A21, 1641. 31. Hasegawa, M.; Hirano, D.; Fujii, M.; Haga, M.; Takezawa, E.; Yamaguchi, S.; Ishikawa, A.; Kagayama, T. J. Polym. Sci. Part A: Polym. Chem. 2013, 51, 575. 32. Takeichi, T.; Agag, T.; Zeidam, R. J. Polym. Sci. Part A: Polym. Chem. 2001, 39, 2633. 33. Takeichi, T.; Saito, Y.; Agag, T.; Muto, H.; Kawauchi, T. Polymer 2008, 49, 1173. 34. Chou, C.-I. ; Liu, Y.-L. J. Polym. Sci. Part A : Polym. Chem.2008, 46, 6509. 35. Ke, L.-L.; Hu, D.; Lu, Y.-B.; Feng, S.; Xie, Y.-Y.; Xu, W.-J. Polym. Degrad. Stab. 2012, 97, 132. 36. Lin, C.-H.; Feng, Y.-R.; Dai, K.-H.; Chang, H.-C.; Juang, T.-Y. J. Polym. Sci. Part A : Polym. Chem.2013, 51, 2686. 37. Liu, C.; Shen, D.; Sebastian, R. M.; Marquet, J.; Schonfeld, R. Macromolecules 2011, 44, 4616. 38. Chen, C.-J.; Yen, H.-J.; Chen, W.-C.; Liou, G.-S. J. Mater. Chem. 2012, 22, 14085. 39. Chang, H.-C.; Lin, H.-T.; Lin, C.-H. Polym. Chem. 2012, 3, 970. 40. Kao, T.-H.; Chen, J.-K.; Cheng, C.-C.; Su, C.-I.; Chang, F.-C. Polymer 2013, 54, 258. 41. Ayala, D.; Lozano, A. E.; Abajo, J. D.; Campa, J. G. D. L. J. Polym. Sci. Part A: Polym. Chem. 1999, 37, 805. 42. Imai, Y.; Itoya, K.; Kanamaru, M.; Kakimoto, M. J. Polym. Sci. Part A: Polym. Chem. 2002, 40, 1790.
摘要: 本論文使用不對稱雙胺單體以其鄰位(ortho)乙基之立體障礙控制雙胺反應性,成功合成含單官能與雙官能胺基的氧代氮代苯并環己烷(Benzoxazine)單體。 將合成之 Benzoxazine 單體應用於聚醯亞胺(Polyimide, PI)製程中,製備出新穎 Poly(benzoxazine imide)s (PBzIs)薄膜材料,並以單官能為 Model reaction 探討 Benzoxazine 結構開環與醯胺酸(Amic acid)結構亞胺化(Imidizaion)反應過程之變化。 製得之薄膜相對於一般聚醯亞胺薄膜(Polyimide, PI)經熱性質分析明顯提升玻璃轉移溫度(Tg)約50-70 oC,並有效降低熱膨脹係數(CTE),可達 24 ppm/oC 的優異性質(O-3),並保有良好的熱穩定性。 此外,於機械性質與疏水性方面皆因導入 Benzoxazine 結構而有所提升,並因導入含磷結構,使薄膜提升阻燃性並可達 UL-94 測試 VTM-0 等級的難燃特性。
URI: http://hdl.handle.net/11455/3172
其他識別: U0005-0108201310484400
文章連結: http://www.airitilibrary.com/Publication/alDetailedMesh1?DocID=U0005-0108201310484400