標題: In Situ Scanning Tunneling Microscopy Study of 3-Mercaptopropanesulfonate Adsorbed on Pt(111) and Electrodeposition of Copper in 0.1 M KClO4 þ 1 mM HCl (pH 3)
作者: Yen, Po-Yu
Tu, Hsin-Ling
Wu, Heng-Liang
Chen, Sihzih
Vogel, Walter
Yau, Shueh-Lin
Dow, Wei-Ping
出版社: American Chemical Society
摘要: In situ scanning tunneling microscopy (STM) was used to examine the spatial structure of adsorbed 3-mercaptopropanesulfonate (MPS) molecules on a Pt(111) electrode in 0.1 M KClO4 t 1 mM HCl t 10_7 M MPS (pH 3). Two ordered MPS structures, Pt(111)_(2 _2) (θ = 0.25) and ( √ 3 _ √ 3)R30_ (θ = 0.33) structures were observed at _0.25 V (vs Ag/AgCl). The former (latter) was more important at more negative (positive) potentials. These MPS structures became a disordered adlayer at E > 0.1 V. These restructuring events could result from a progressive increase of the surface coverage of MPS with potential. Shifting the potential negatively could restore the ordered structures of ( √ 3_ √ 3)R30_ and (2_2), but the rather strong Pt-MPS made it difficult for MPS admolecules to desorb from the Pt(111) electrode. By contrast, the MPS adlayer seen in 0.1 M HClO4 was always disordered, regardless of the potential of Pt(111) electrode. (Tu et al., J. Electrochem. Soc. 2010, 157, D206.) It is reasonable to state that potential control, pH, and/or countercations to the sulfonate group of the MPS admolecule could be important in guiding the adsorption of MPS molecules on Pt(111) electrode. Strongly adsorbed MPS molecules on the Pt(111) electrode could impede the rate of Cu2t reduction, thereby inhibiting rather than accelerating electrodeposition of copper under the present conditions. Real-time STM imaging revealed random nucleation of copper adatoms on Pt(111), followed by lateral growth of Cu nuclei upon further deposition. Segregated domains of ( √ 3_ √ 3)R30_, ascribable to MPS and chloride adspecies, were observed atop a monolayer of Cu deposit prior to the commencement of bulk Cu deposition. With a small overpotential (η < 20 mV), multilayer copper was electroplated on Pt(111) in a layered manner, producing atomically smooth Cu deposit capped by patches of (3 _ 3) MPS. By contrast, the Cu deposit on MPS-modified Pt(111) in 0.1 M HClO4 was decidedly rough, as reported earlier.
URI: http://hdl.handle.net/11455/41014
ISSN: 1932-7447
顯示於類別:化學工程學系所

文件中的檔案:
沒有與此文件相關的檔案。


在 DSpace 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。