標題: Effects of electrolytic zirconium oxide coating on hydrogen permeation of AISI 430 stainless steel
作者: Yen, S.K.
顏秀崗
Huang, I.B.
Yen, Z.S.
關鍵字: blistering
retarding effect
Type 430 stainless steel
zirconium oxide
coating
commercial pure titanium
brittle-fracture
embrittlement
diffusion
films
retardation
mechanism
metals
ph
期刊/報告no:: Corrosion, Volume 56, Issue 10, Page(s) 998-1004.
摘要: Through Devanathan hydrogen permeation tests and a mathematical analysis, the retarding effect of electrolytic deposition of zirconium oxide (ZrO2) films on the hydrogen-induced blistering or entry was investigated. The permeation test has indicated that the diffusion coefficient in a metal sheet of AISI 430 (UNS S43000) stainless steel (D-m) was 1.73 x 10(-8) cm(2)/s and that in ZrO2 (D-Zr) was 4.74 x 10(-16) cm(2)/s. Also, the subsurface hydrogen concentration on the metal (C-h(m); 2.29 x 10(-5) mol/cm(3)) was reduced to (C-h(m) = 0.64 x 10(-5) mol/cm(3)) caused not only by a high concentration ratio (K; 8.022) of the oxide film to the metal but also by the extremely low value of D-Zr. Blistering was found on the uncoated specimen after the hydrogen permeation test but was not found on the coated specimen. The electrolytic deposition of ZrO2 film on the AISI 430 stainless steel demonstrated the retarding effect on hydrogen entry and the occurrence of blistering.
URI: http://hdl.handle.net/11455/43786
ISSN: 0010-9312
Appears in Collections:材料科學與工程學系

文件中的檔案:

取得全文請前往華藝線上圖書館



Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.