標題: Cathodic reactions of electrolytic hydroxyapatite coating on pure titanium
作者: Yen, S.K.
Lin, C.M.
關鍵字: cathodic reaction
electrolytic hydroxyapatite
calcium phosphates
期刊/報告no:: Materials Chemistry and Physics, Volume 77, Issue 1, Page(s) 70-76.
摘要: The cathodic reactions of electrolytic HA (hydroxyapatite) coating on pure titanium in the mixed solution of Ca(NO3)(2).4H(2)O and NH4H2PO4 were investigated by the cathodic polarization tests in Ca(NO3)(2).4H(2)O, NH4H2PO4 and HCl aqueous solution. The deposited films at various applied current densities were characterized by XRD analysis and SEM observations. XRD analysis revealed Ca(HPO3H)(2).H2O at a -0.7 V, CaHPO4.2H(2)O (DCPD) and Ca-10(PO4)(6)(OH)(2) (HA) at -1.25 V. SEM observations showed hydrogen bubble effect on deposition of HA at -1.55 V The cathodic reactions in the mixed solution were verified into four regions: (1) O-2 + 2H(2)O + 4e(-) --> 4OH(-)(-0.1 to -0.3 V); (2) H2PO4- + H2O + 2e(-) --> H2PO3- + 2OH(-) (-0.3 to -1.1 V); (3) H2PO4- + e(-) --> HPO42- + (1)/(2) H-2 and H2PO4- + 2e(-) --> PO43- + H-2 (- 1.1 to - 1.5 V); (4) 2H(2)O + 2e(-) --> H-2+2OH(-) (-1.5 to -3.0 V). A pure HA deposition film can be obtained after annealed at 300 degreesC for 4 h. (C) 2002 Elsevier Science B.V. All rights reserved.
ISSN: 0254-0584
Appears in Collections:材料科學與工程學系



Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.