標題: Mechanism of electrolytic ZrO2 coating on commercial pure titanium
作者: Yen, S.K.
顏秀崗
關鍵字: mechanism
electrolytic ZrO2 coating
titanium
期刊/報告no:: Materials Chemistry and Physics, Volume 63, Issue 3, Page(s) 256-262.
摘要: Through cathodic polarization tests of commercial pure titanium electrode in H2O, HCl, NaNO3, ZrO(NO3)(2) and a mixture of HCl and NaNO3 aqueous solutions, respectively, the mechanism of electrolytic deposition of ZrO2 on commercial pure Ti has been investigated. It is found that the cathodic polarization curves in 0.0125 M ZrO(NO3)(2) should be divided into three stages: the first, the reduction of dissolved H+ (2H(+) + 2e(-) --> H-2) the second, the diffusion limit of H+ in the first stage (concentration polarization), and the third, the reduction of H2O (2H(2)O + 2e(-) H-2 + 2OH(-)). The electrolytic deposition experiments show the highest Faradaic coating efficiency of 26% at the current density 1 mA cm(-2) which is at the transition stage between the diffusion limit current density (i(L)) of H+ (2nd stage) and the onset H2O reduction, since H+ ions are depleted and thus much more OH- ions are provided to form Zr(OH)(4) gel on the cathodic surface. In the third stage, many Hz bubbles are formed and the Hz bubbles latter push the formed Zr(OH)(4) away form the cathodic surface. A good adhesion to Ti substrate is obtained after coated specimens annealed at less than or equal to 973 K, and the crystallization of the coating to form tetragonal ZrO2 can occur at 723 K. (C) 2000 Elsevier Science S.A. All rights reserved.
URI: http://hdl.handle.net/11455/43848
ISSN: 0254-0584
文章連結: http://dx.doi.org/10.1016/s0254-0584(99)00232-1
Appears in Collections:材料科學與工程學系

文件中的檔案:

取得全文請前往華藝線上圖書館



Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.