標題: Electrolytic Al2O3/Y2O3 double-layer coating on IN617 superalloy
作者: Hsu, C.T.
顏秀崗
Chang, C.C.
Chang, T.N.
Yen, S.K.
關鍵字: IN617 superalloy
Al2O3
Y2O3
YAG
electrolytic deposition
deposition
oxide
期刊/報告no:: Surface & Coatings Technology, Volume 200, Issue 22-23, Page(s) 6611-6617.
摘要: In this study, IN-617 superalloy was coated with Al2O3/Y2O3 double-layer films by electrolytic deposition in AI(NO3)(3) and Y(NO3)(3) aqueous solutions. Characterization of coated specimens was conducted by thermo-gravitational analysis (TGA), X-ray diffraction (XRD), scanning electron microscopy (SEM), aqueous corrosion tests in 3.5% NaCl, hot corrosion test in 2 mg/cm(2) Na2SO4 contained environment at 850 degrees C, and high temperature oxidation test at 1000 degrees C in air. The Y2O3/Al2O3 double layer coating revealed the composite crystal structures of Y2O3, Al2O3 and yttrium-aluminum garnet (YAG). Also YAG powders can be prepared by collecting and annealing the coating film. The Y2O3/Al2O3 coating film revealed the efficient retarding effects on the oxidation (NiO) of In617 superalloy in air at 1000 degrees C, since the coating film prohibited the formation of NiO and promoted the growth of Cr2O3. Also, it revealed more corrosion resistance in 3.5% NaCl aqueous solution and more hot corrosion resistance in Na2SO4 contained environment at 850 degrees C. (c) 2005 Elsevier B.V. All rights reserved.
URI: http://hdl.handle.net/11455/43863
ISSN: 0257-8972
文章連結: http://dx.doi.org/10.1016/j.surfcoat.2005.11.111
Appears in Collections:材料科學與工程學系

文件中的檔案:

取得全文請前往華藝線上圖書館



Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.