標題: Study of 375 nm ultraviolet InGaN/AlGaN light-emitting diodes with heavily Si-doped GaN transition layer in growth mode, internal quantum efficiency, and device performance
作者: Huang, S.C.
洪瑞華
Shen, K.C.
Wuu, D.S.
Tu, P.M.
Kuo, H.C.
Tu, C.C.
Horng, R.H.
武東星
關鍵字: threading dislocations
reduction
masks
movpe
期刊/報告no:: Journal of Applied Physics, Volume 110, Issue 12.
摘要: High performance 375 nm ultraviolet (UV) InGaN/AlGaN light-emitting diodes (LEDs) were demonstrated with inserting a heavy Si-doped GaN transition layer by metal-organic chemical vapor deposition. From transmission electron microcopy (TEM) image, the dislocation densities were significantly reduced due to the existence of the heavily Si-doping growth mode transition layer (GMTL), which results in residual stress relaxation and 3D growth. The internal quantum efficiency (IQE) of the LEDs with GMTL was measured by power-dependent photoluminescence (PL) to be 40.6% higher than ones without GMTL. The GMTL leads to the superior IQE performance of LEDs not only in decreasing carrier consumption at nonradiative recombination centers but also in partially mitigating the efficiency droop tendency. When the vertical-type LED chips (size: 1 mm x 1 mm) was driven with a 350 mA injection current, the output powers of the LEDs with and without GMTL were measured to be 286.7 and 204.2 mW, respectively. A 40.4% enhancement of light output power was achieved. Therefore, using the GMTL to reduce dislocations would be a promising prospective for InGaN/AlGaN UV-LEDs to achieve high IQE. (C) 2011 American Institute of Physics. [doi: 10.1063/1.3669377]
URI: http://hdl.handle.net/11455/43991
ISSN: 0021-8979
文章連結: http://dx.doi.org/10.1063/1.3669377
顯示於類別:材料科學與工程學系

文件中的檔案:
沒有與此文件相關的檔案。


在 DSpace 系統中的文件,除了特別指名其著作權條款之外,均受到著作權保護,並且保留所有的權利。