標題: Magnetic properties and microstructure of (Fe0.5+yPt0.5-y)(z)B100-z (y=0-0.2; z=82 and 84) melt spun ribbons
作者: Chang, C.W.
Chang, H.W.
Chiu, C.H.
Chen, C.H.
Chang, W.C.
Ouyang, H.
Liu, C.C.
關鍵字: permanent magnet
nanocomposite
melt spinning
FePt
FePtB
exchange-coupling
期刊/報告no:: Journal of Iron and Steel Research International, Volume 13, Page(s) 273-278.
摘要: The Fe-B/FePt-type nanocomposite ribbons with strong exchange-coupling and high permanent magnetic properties have been developed by the melt-spinning method. For ternary (Fe0.5+yPt0.5-y)(z)B100-z (y=0-0.2; z=82 and 84), multiple phases, namely gamma(1), Fe2B and Fe3B, with nanoscaled grain sizes (25-35 nm) can readily form in ribbons after an isothermal annealing at 500 T. Strong exchange-coupling between grains was found in these ribbons, giving rise to an enhancement of not only the remanence but also the maximum energy product. An H-i(c) of more than 12 kOe has been obtained in (Fe0.6Pt0.4)(82)B-18 (B-r=6.6 kG, (BH)(max)=8.9 MGOe), and a B-r of 9.4 kG, H-i(c) of 7.5 kOe and (BH)(max) of 14.0 MGOe can be achieved in (Fe0.675Pt0.325)(84)B-16. Magnetically soft Fe2B and Fe3B were found to present in the matrix, as evidenced by high resolution transmission electron microscopy. Because of the higher saturation magnetization of Fe3B than Fe2B, the coexistence of Fe3B with Fe2B and gamma(1) phases was believed the main cause to result in the improved remanence and magnetic energy product of the (Fe0.675Pt0.325)(84)B-16 ribbons.
URI: http://hdl.handle.net/11455/70058
ISSN: 1006-706X
文章連結: http://dx.doi.org/10.1016/s1006-706x(08)60193-4
Appears in Collections:期刊論文

文件中的檔案:

取得全文請前往華藝線上圖書館



Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.