標題: Preparation and characterization of platinum/iron contained hydroxyapatite/carbon black composites
關鍵字: Iron contained hydroxyapatite
Carbon blacks
Methanol oxidation reaction (MOR)
Carbon mono-oxide (CO) poisoning
Electrochemical surface area (ECSA)
摘要: In this report, calcium ions in the porous hydroxyapatite (HAp) microspheres are partially exchanged with ferrous ions to form iron contained hydroxyapatite (FeHAp) on which Pt ions in H2PtCl6 solution are reduced to form Pt/FeHAp catalyst and finally mixed with carbon blacks to derive Pt/FeHAp/C catalysts. They exhibit the characteristics of Pt (1 1 0) facet with a sharp desorption peak at −0.109 V (vs. Ag/AgCl), the electrochemical surface area (ECSA) ranging from 73 to 224 m2 g−1 with little CO poisoning effect on Pt, and the mass activity ranging from 6.88 to 28.99 A gPt−1 in methanol oxidation reaction (MOR) at 0.4 V (vs. Ag/AgCl). Besides, Pt/FeHAp reveals the lower onset potential in CO-stripping than Pt/C. These better performances of Pt/FeHAp/C catalysts, compared with Pt/C, are also related to the Pt (1 1 0) facet, the content of Fe, and the coexistence of Pt0 and Pt2+ in Pt/FeHAp.
URI: http://hdl.handle.net/11455/84949
文章連結: http://dx.doi.org/10.1016/j.ijhydene.2013.08.003
Appears in Collections:材料科學與工程學系

文件中的檔案:

取得全文請前往華藝線上圖書館



Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.