dc.description.abstractIn this study, cellulose acetate (CA)/titanium dioxide (TiO2) hybrid membranes were prepared. To obtain hybrid membranes, we used acetone/NMP/DMF wt% = 15:0.5:0.5 as mix solvents and make them on glass plate by 220μm scraper. Different weight ratio of TiO2 to CA were investigated and the relative membrane properties were measured and compared. The shear stress and shear strain of hybrid membranes were increased with increasing TiO2/CA ratio. Because of the increasing membrane thickness, water transportation resistance was increasing, too. The TiO2 : CA=1:10 membrane had the highest water flux.en_US
dc.description.abstract本研究以醋酸纖維(cellulose Acetate, CA)與二氧化鈦(titanium dioxide, TiO2)於不同比例摻混製備薄膜。製備過程中,以丙酮╱NMP╱DMF比例為15:0.5:0.5之混合液為混合溶劑,厚度220μm之刮刀於玻璃平板上製備二氧化鈦╱醋酸纖維參混膜。本研究利用ATR-FTIR與XRD驗證參混膜中二氧化鈦之存在、TGA測量二氧化鈦所佔比例、拉力測試觀察參混二氧化鈦後拉力增加的幅度。隨著二氧化鈦比例增加,薄膜機械強度也隨之上升。在直接滲透應用方面,由於刮出來的薄膜厚度隨二氧化鈦比例提高而增加,造成薄膜質傳阻力增加,薄膜水通量上升趨勢為先高後低。薄膜水通量以摻混10%二氧化鈦為最高。zh_TW
dc.description.tableofcontents致謝………………………………………………………………………...….. i 中文摘要……………………………………………………………………… ii 英文摘要…………………….……………………………………………..… iii 目錄………………………….……………………………………………….. iv 表目錄……………………….….……………………………………………. vi 圖目錄……………………….………………………………………………. vii 第一章 導論…....…………………………..………..……………………….1 1.1 緒論…………………………..………..………...………………….1 1.2 逆滲透與直接滲透…………………..………….………………….1 1.3 醋酸纖維薄膜改良…………………..………….………………….2 1.4 二氧化鈦摻混………………………..………….………………….3 1.5 研究目的……………………………..………….………………….3 第二章 實驗方法…………………....……………………………………….5 2.1 實驗藥品……...…………….……………...……………………….5 2.2 薄膜製備……...…………………………………………………….6 2.3 含水率測試……...………………………………………………….6 2.4 減弱全反射紅外光譜儀…………………………………………....6 2.5 X光繞射儀………………………...…………….…........................7 2.6 熱重損失分析儀……………………………………........................7 2.7 場發射掃描式電子顯微鏡…………………………........................7 2.8 機械性質……...…………………………………………………….7 2.9 直接滲透……...…………………………...….…………………….8 第三章 結果與討論…...…………………….……………………………….9 3.1 薄膜參混基本性質..……...……………………..………………….9 3.2 ATR-FTIR測試..…………………….........……..……………….. .9 3.3 XRD測試…...…………...……...…………………..…………..….9 3.4 SEM…...………………………...……………………..………......10 3.5 TGA測試……………………….……....……………………...….10 3.6 機械性質分析……………………..……...………...…………......10 3.7 直接滲透…………………………….........………………….........11 第四章 結論...…………………………………………………………...….12 參考文獻…...…………………………………………………………...…….13 表目錄 頁次 表一、直接使用含TiO單體製作薄膜………………………...…………….17 表二、使用高分子或先聚合成高分子後,再加入TiO2製成參混薄膜……...18 表三、摻入TiO2製作薄膜文獻之實驗目的………………...…………….….19 表四、不同比例TiO2參混薄膜的厚度及含水率………...…………….…….20 圖目錄 頁次 圖一、醋酸纖維之結構式………...……………………………………….…….21 圖二、直接滲透之操作示意圖...………………………………………….…….22 圖三、不同TiO2重量比例之混成薄膜的ATR-FTIR光譜圖……..……….……..23 圖四、各種不同TiO2重量比例之混成薄膜的XRD圖譜………………………..24 圖五、各種不同TiO2重量比例之混成薄膜的SEM圖……………...……….…..25 圖六、各種不同TiO2重量比例之混成薄膜的TGA圖……………………….….26 圖七、各種不同TiO2重量比例之參混薄膜的拉力測試結果……………….….27 圖八、各種不同TiO2重量比例之參混薄膜的拉伸長度測試結果……………..28 圖九、各種不同TiO2重量比例之混成薄膜於直接滲透程序中的水通量結果….29 圖十、各種不同TiO2重量比例之混成薄膜於直接滲透程序中的鹽阻絕效果.….30zh_TW
dc.language.isoen_USzh_TW
dc.publisher化學工程學系所zh_TW
dc.subject直接滲透zh_TW
dc.subjectforward osmosisen_US
dc.subject醋酸纖維zh_TW
dc.subject二氧化鈦zh_TW
dc.subject摻混zh_TW
dc.subjectcellulose acetateen_US
dc.subjecttitanium dioxideen_US
dc.subjecthybriden_US
dc.titleTitanium dioxide╱Cellulose acetate hybrid membrane for forward osmosisen_US
dc.title二氧化鈦╱醋酸纖維混成薄膜於直接滲透程序之應用zh_TW
dc.typeThesis and Dissertationzh_TW
item.openairecristypehttp://purl.org/coar/resource_type/c_18cf-
item.fulltextno fulltext-
item.cerifentitytypePublications-
item.grantfulltextnone-
item.languageiso639-1en_US-
item.openairetypeThesis and Dissertation-
Appears in Collections:化學工程學系所
Show simple item record
 

Google ScholarTM

Check


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.