標題: Carbon black containing interpenetrating polymer networks based on unsaturated polyester/epoxy III: thermal and pyrolysis analysis
作者: Shih, Y.F.
鄭如忠
Jeng, R.J.
Wei, K.M.
關鍵字: carbon black;IPN;epoxy;unsaturated polyester;DSC;Py-GC-MS;adiabatic calorimeter;heat of combustion;chromatography mass-spectrometry;gas chromatography;flame retardants;fire-retardant;epoxy-resins;mechanical-properties;magnesium-hydroxide;degradation;products;decomposition
Project: Journal of Analytical and Applied Pyrolysis
期刊/報告no:: Journal of Analytical and Applied Pyrolysis, Volume 70, Issue 1, Page(s) 129-141.
摘要: 
In this study, carbon black flame retardants were chosen to improve the flame resistance of the interpenetrating polymer networks (IPNs) based on unsaturated polyester/epoxy due to the expansion of carbon black at elevated temperatures. The results of DSC reveal that the Tg of the IPN sample became indistinct as the carbon black was added. This is due to the increase of inorganic content. It was also found from adiabatic calorimeter that the heat of combustion of the IPN sample was decreased by the addition of carbon black flame retardants. The results of Py-GC-MS reveal that the degradation of IPNs was derived from the non-interfering thermal decomposition processes of the respective IPN components. Moreover, the degradation process of IPN was inhibited as the carbon black was added to the IPN. This led to the lower content of low molecular weight compounds and fewer species of degradation products. More detailed decomposition processes were obtained from the above-mentioned characterization, which are consistent with previous DMA and TGA studies. (C) 2002 Elsevier Science B.V. All rights reserved.
URI: http://hdl.handle.net/11455/41827
ISSN: 0165-2370
DOI: 10.1016/s0165-2370(02)00102-x
Appears in Collections:化學工程學系所

Show full item record
 

Google ScholarTM

Check

Altmetric

Altmetric


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.