標題: Characterization and bond strength of electrolytic HA/TiO2 double layers for orthopedic applications
作者: Lin, C.M.
顏秀崗
Yen, S.K.
關鍵字: hydroxyapatite coatings;structural characterization;osteoblasts;behavior;expression;deposition;substrate;cultures;receptor;surface;cells
Project: Journal of Materials Science-Materials in Medicine
期刊/報告no:: Journal of Materials Science-Materials in Medicine, Volume 15, Issue 11, Page(s) 1237-1246.
摘要: 
Insufficient bonding of juxtaposed bone to an orthopedic/dental implant could be caused by material surface properties that do not support new bone growth. For this reason, fabrication of biomaterials surface properties, which support osteointegration, should be one of the key objectives in the design of the next generation of orthopedic/dental implants. Titanium and titanium alloy have been widely used in several bioimplant applications, but when implanted into the human body, these still contain some disadvantages, such as poor osteointegration (forming a fibrous capsule), wear debris and metal ion release, which often lead to clinical failure. Electrolytic hydroxyapatite/titanium dioxide (HA/TiO2) double layers were successfully deposited on titanium substrates in TiCl4 solution and subsequently in the mixed solution of Ca(NO3)(2) and NH4H2PO4, respectively. After annealing at 300degreesC for 1 h in the air, the coated specimens were evaluated by dynamic cyclic polarization tests, immersion tests, tensile tests, surface morphology observations, XRD analyses and cells culture. The adhesion strength of the HA coating were improved by the intermediate coating of TiO2 from 11.3 to 46.7 MPa. From cell culture and immersion test results, the HA/TiO2 coated specimens promoted not only cells differentiation, but also appeared more bioactive while maintaining non-toxicity. (C) 2004 Kluwer Academic Publishers.
URI: http://hdl.handle.net/11455/43809
ISSN: 0957-4530
DOI: 10.1007/s10856-004-5678-8
Appears in Collections:材料科學與工程學系

Show full item record
 

Google ScholarTM

Check

Altmetric

Altmetric


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.