|標題:||Fabrication and characterization of PPO/PVP blend carbon molecular sieve membranes for H2/N2 and H2/CH4 separation||作者:||Itta, Arun Kumar
|關鍵字:||Polymer;Blending;Spin coating;CMS membrane;Gas separation||出版社:||Elsevier B.V.||Project:||Journal of Membrane Science, Volume 372, Issue 1-2, Page(s) 387-395.||摘要:||
Through a spin-coating technique, a high performance carbon molecular sieve (CMS) membranes were fabricated from thermally stable polymer polyphenylene oxide (PPO) and thermally labile polymer poly vinylpyrrolidone (PVP). The permeation results show that the small gas molecules (H2, CO2, N2, and CH4) transport mechanism is dominated by the molecular sieving effect. The permeation performances have a strong dependency upon polymer concentration and pyrolysis temperature. The best performance for hydrogen permeability obtained with PPO 15 PVP pyrolyzed at 700 °C was 1121 Barrer (1 Barrer = 1 × 10−10 cm3 (STP) cm/[cm2 s cm Hg]) and the values of selectivity for gas pairs such as H2/N2 and H2/CH4 were 163.9 and 160.9, respectively. The correlation factor of permselectivity of H2/N2 and H2/CH4 gas pairs obtained from PPO and PPO/PVP derived CMS membranes were above the Robeson (2008) upper bound. The addition of thermally labile PVP creates diffusion pathways and controls selectivities for the CMS membranes derived from PPO 10 PVP and PPO 15 PVP.
|Appears in Collections:||環境工程學系所|
Show full item record
TAIR Related Article
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.