標題: Effect of Pt underlayer on the coercivity of FePt sputtered film
作者: Hsu, C.W.
Chen, S.K.
Liao, W.M.
Yuan, F.T.
Chang, W.C.
Tsai, J.L.
關鍵字: FePt;thin film;Pt underlayer;thermal expansion coefficient;residual;stress;thin-films;magnetic-properties;temperature;microstructure;layer;texture;order
Project: Journal of Alloys and Compounds
期刊/報告no:: Journal of Alloys and Compounds, Volume 449, Issue 1-2, Page(s) 52-55.
摘要: 
Magnetic properties of the FePt/Pt bilayers with Pt underlayer were investigated. By introducing the Pt underlayer, coercivity H-c and ordering parameter K of the film were enhanced by about of 50%. After a low-temperature annealing process at only 400 degrees C, H-c was increased from 6.26 to 9.78 kOe and K was increased from 0.586 to 0.844. Theoretical calculations indicated that there existed a compressive stress in the FePt film. The stress was found to release with the increase in thickness of the Pt underlayer. The increase in lattice parameter a(FePt) and the decrease in lattice parameter c(FePt) were closely related to the relaxed compressive stress in the FePt film as the thickness of Pt underlayer was increased. The relaxed compressive stress can account for the enhancement in the ordering parameter and the coercivity of the FePt/pt bilayer materials. (C) 2006 Elsevier B.V. All rights reserved.
URI: http://hdl.handle.net/11455/69652
ISSN: 0925-8388
DOI: 10.1016/j.jallcorn.2006.01.113
Appears in Collections:期刊論文

Show full item record
 
TAIR Related Article

Google ScholarTM

Check

Altmetric

Altmetric


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.