標題: Intercalation of layered double hydroxides by poly(oxyalkylene)-amidocarboxylates: tailoring layered basal spacing
作者: Lin, J.J.
Juang, T.Y.
關鍵字: layered double hydroxides;intercalation;amidoacid;mechanical-properties;clay nanocomposites;montmorillonite;hybrids;delamination;polystyrene;anion;acid
Project: Polymer
期刊/報告no:: Polymer, Volume 45, Issue 23, Page(s) 7887-7893.
摘要: 
Mg-Al layered double hydroxides (LDHs) were intercalated with various molecular-weight poly(oxypropylene)-bis-amidoacid salts LDHs at 120 degreesC and under N-2 atmosphere in an autoclave to afford a series of organoclays with a maximal basal spacing of 92 Angstrom, revealed by X-ray diffraction and transmission electron microscopy analyses. The unusually wide interlayer spacing was ascribed to the self-alignment of the hydrophobic POP backbone in the layer confinement. In contrast, the intercalation of poly(oxyethylene)-bis-amidoacids (POE-acid) afforded a low basal spacing (7.8 Angstrom) due to their oxyethylene-backbone interaction with the layered surface. The resultant POP- and POE-acid intercalated LDHs also exhibited different dispersing properties in toluene or water. Particularly, the organically-modified and spaceenlarged hybrids with a proper amount of the embedded POPs possessed an amphiphilic property of lowering the toluene/water interfacial tension. (C) 2004 Elsevier Ltd. All rights reserved.
URI: http://hdl.handle.net/11455/71136
ISSN: 0032-3861
DOI: 10.1016/j.polymer.2004.09.031
Appears in Collections:期刊論文

Show full item record
 

Google ScholarTM

Check

Altmetric

Altmetric


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.