標題: Evaluation of hillock-like deposition behaviour of HVOF thermal spray coatings using rotary shutter procedure
作者: Hsiao, W.T.
Liao, W.H.
Su, C.Y.
Leu, M.S.
關鍵字: Thermal spraying;HVOF;Coatings;Rotary shutter;Hillock-like;WC/Co;wc-co coatings;titania coatings;temperature;velocity;microstructure;parameters;strength;hardness;alloy
Project: Surface Engineering
期刊/報告no:: Surface Engineering, Volume 25, Issue 4, Page(s) 313-318.
摘要: 
Evaluation of hillock-like deposition behaviour of WC/Co coatings was performed using a rotary shutter procedure coupled with 100 passes of high velocity oxy fuel thermal spraying. During the spraying procedure, a DPV 2000 in situ diagnostic instrument was used to monitor the temperature and velocity of inflight particles. The microstructure of the coatings was analysed using an optical microscope to monitor the porosity and thickness distributions at various positions of the hillock-like coatings. A 7(.)1% porosity was observed at the centre of the hillock-like coatings, and a 10% porosity was observed at the edge, each at a spraying distance of 200 mm. The centre area of hillock-like coatings exhibited almost a 30% decrease in porosity compared to the edge area. The results indicate a higher quality structure at the centre area of the hillock-like coatings.
URI: http://hdl.handle.net/11455/71378
ISSN: 0267-0844
DOI: 10.1179/174329408x326416
Appears in Collections:期刊論文

Show full item record
 

Google ScholarTM

Check

Altmetric

Altmetric


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.