標題: Wear and Corrosion Investigation on the Electrodeposited Ni-P Coating
作者: Lee, H.B.
Lin, C.S.
Wuu, D.S.
Lee, C.Y.
關鍵字: Nickel;Friction Mechanism;Corrosion;resistance;behavior;alloy;films;composites;deposits
Project: Tribology Transactions
期刊/報告no:: Tribology Transactions, Volume 54, Issue 4, Page(s) 497-504.
摘要: 
The wear and corrosion characteristics of an electrodeposited Ni-P coating were studied using a block-on-ring wear tester. The testing environments included dry wear and immersion wear in a 5 wt% NaCl water solution bath to simulate the corrosive atmosphere. The wear behavior is discussed in terms of the friction coefficient, wear rate, and surface roughness. Under boundary lubrication, the wear mechanism changed from both adhesive and abrasive wear for dry contact to mostly abrasive wear in corrosive salt water. The corrosion pits and corrosion film formed during accelerated corrosion wear testing not only lowered the friction coefficient but decreased the surface roughness. However, due to the accelerated pitting corrosion and removal of the corrosion film, the weight loss was slightly increased. Finally, the X-ray photoelectron spectroscopy (XPS) and transmission electron microscopy (TEM) analyses confirmed the formation of a porous corrosion film after the wear test in salt water.
URI: http://hdl.handle.net/11455/71549
ISSN: 1040-2004
DOI: 10.1080/10402004.2011.568711
Appears in Collections:期刊論文

Show full item record
 

Google ScholarTM

Check

Altmetric

Altmetric


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.