標題: Solid solution coating of (TiVCrZrHf)N with unusual structural evolution
關鍵字: Coating materials;Nitride materials;Microstructure
Project: Surface and Coatings Technology, Volume 217, Page(s) 84-87.
摘要: 
In this study, we investigated the microstructure of (TiVCrZrHf)N multi-element coating deposited on Si(100) substrate by magnetron sputtering system. Interestingly, the film showed an unusual structure evolution. A continuous and amorphous initial (TiVCrZrHf)N layer formed on the substrate. As film thickness increased, randomly oriented small (TiVCrZrHf)N grains formed, followed by the development of columnar grains with FCC crystal phase. In contrast to previous studies, the nitride coatings grew on substrates with a 270-nm amorphous interlayer. Under appropriate parameters, the occurrence of the unusual microstructure could be attributed to the sluggish diffusion of the multi-principal components. The maximum hardness of 33.5 GPa was obtained when coating was deposited under substrate bias of − 100 V and at substrate temperatures of 723 K.
URI: http://hdl.handle.net/11455/84935
DOI: 10.1016/j.surfcoat.2012.11.077
Appears in Collections:材料科學與工程學系

Show full item record
 

Google ScholarTM

Check

Altmetric

Altmetric


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.