標題: Microstructure and magnetic properties of FePt film with combined MoC/(Mg–X)O (X=Cu, Ni, Co) intermediate layers
作者: 蔡佳霖
Jai-Lin Tsai
Jie-Lin Tzeng
Keng-Chun Hu
Hsu-Kang Li
Zu-Yu Pan
Yuan-Shuo Chang
Chang-Chun Liao
出版社: JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS
Project: Journal of Magnetism and Magnetic Materials, Volume 422, 15 January 2017, Pages 262-270
摘要: 
The magnetic properties and microstructure of FePt films grown on MoC layer and MoC/(Mg–X)O (X=Cu, Ni, Co) combined intermediate layers were studied. The (Mg–X)O (X=Cu, Ni, Co) layer with thickness of 5 nm was deposited on CrRu seed layer at 395 °C. The CrRu (200) texture was enhanced which may due to well grains growth in specific orientation and small lattice mismatch with (Mg–X)O (X=Cu, Ni, Co). Finally, the FePt/MoC layers were deposited on (Mg–X)O layer at 425 °C. Using MoC/MgCuO combined intermediate layers, the rocking width of FePt (001) and CrRu (200) diffraction peak were changed from 7.1° to 6.1°, and 5.7° to 3.8°, respectively. For MoC/MgCoO dual intermediate layers, the rocking width of FePt (001) and CrRu (200) diffraction peak were 6.7° and 4.1°. The FePt/MoC/MgCoO film illustrates perpendicular magnetic anisotropy with out-of plane coercivity of 9.3 kOe which is higher than FePt film deposited on MoC layer (8.5 kOe) and the in-plane loops is linear. From microstructure, the FePt grains were more separated on MoC/(Mg–X)O (X=Cu, Ni, Co) combined intermediate layers.
URI: http://hdl.handle.net/11455/95695
DOI: 10.1016/j.jmmm.2016.09.003
Appears in Collections:材料科學與工程學系

Files in This Item:
File Description SizeFormat Existing users please Login
1-s2.0-S0304885316308393-main.pdf期刊論文4.18 MBAdobe PDFThis file is only available in the university internal network    Request a copy
Show full item record
 

Google ScholarTM

Check

Altmetric

Altmetric


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.