標題: 以尿素玻璃法製備鈦鈮氮氧複材於可見光光催化染料降解之研究
Urea-Glass Preparation of Ti-Nb Nitride-Oxide Composites for Visible-Light Dye Photodegradation
作者: 蔡季剛
Chi-Gang Tsai
關鍵字: 尿素玻璃法;氮摻雜;可見光催化;鈦鈮氮氧複材;urea-glass;dye photodegradation;Ti-Nb Nitride-Oxide Composites
引用: [1] K. T. Meilert, D. Laub, and J. Kiwi,'Photocatalytic self-cleaning of modified cotton textiles by TiO2 clusters attached by chemical spacers,'Journal of Molecular Catalysis A: Chemical, 237, 101-108 (2005). [2] H. A. Foster, I. B. Ditta, S. Varghese, and A. Steele,'Photocatalytic disinfection using titanium dioxide: spectrum and mechanism of antimicrobial activity,'Applied Microbiology and Biotechnology, 90, 1847-1868 (2011). [3] S. A. Ansari, M. M. Khan, M. O. Ansaric, and M. H. Cho,'Nitrogen-doped titanium dioxide (N-doped TiO2) for visible light photocatalysis,'New Journal of Chemistry, 40, 3000-3009 (2016). [4] X. Q. Ma, Y. Chen, J. Lee, C. F. Yang, and X. L. Cui,'In situ formation of NbOx@NbN microcomposites: seeking potential in photocatalytic and Li-ion battery applications,'New Journal of Chemistry, 42, 1300-1308 (2018). [5] A. L. Linsebigler, G. Q. Lu, and J. T. Yates,'Photocatalysis on TiOn surfaces: principles, mechanisms, and selected results,'Chemical Reviews, 95, 735-758 (1995). [6] M. R. Hoffmann, S. T. Martin, W. Y. Choi, and D. W. Bahnemann, 'Environmental Applications of Semiconductor Photocatalysis,'Chemical Reviews, 95, 69-96 (1995). [7] Y. W. Wang, Y. Huang, W. K. Ho, L. Z. Zhang, Z. G. Zou, and S. C. Lee, 'Biomolecule-controlled hydrothermal synthesis of C–N–S-tridoped TiO2 nanocrystalline photocatalysts for NO removal under simulated solar light irradiation,'Journal of Hazardous Materials, 169, 77-87 (2009). [8] C. Su, C. M. Tseng, L. F. Chen, B. H. You, B. C. Hsu, and S. S. Chen, 'Sol–hydrothermal preparation and photocatalysis of titanium dioxide,'Thin Solid Films, 498, 259-265 (2006). [9] H. X. Li, Z. Bain, J. Zhu, D. Zhang, G. Li, Y. Huo, H. Li and Y. Lu, 'Mesoporous titania spheres with tunable chamber stucture and enhanced photocatalytic activity,'Journal of the American Chemical Society, 129, 8406-8407 (2007). [10] D. H. Chen, L. Cao, F. Z. Huang, P. Imperia, Y. B. Cheng, and R. A. Caruso,'Synthesis of monodisperse mesoporous titania beads with controllable diameter, high surface areas, and variable pore diameters (14-23 nm),' Journal of the American Chemical Society, 132, 4438-4444 (2010). [11] D. Behar and J. Rabani,'Kinetics of hydrogen production upon reduction of aqueous TiO2 nanoparticles catalyzed by Pd0, Pt0, or Au0 coatings and an unusual hydrogen abstraction; steady state and pulse radiolysis study,'Journal of Physical Chemistry B, 110, 8750-8755 (2006). [12] Z. Yi, W. Wei, S. Lee, and J. H. Gao,'Photocatalytic performance of plasma sprayed Pt-modified TiO2 coatings under visible light irradiation,'Catalysis Communications, 8, 906-912 (2007). [13] K. Maeda and K. Domen,'New non-oxide photocatalysts designed for overall water splitting under visible light,'Journal of Physical Chemistry C, 111, 7851-7861 (2007). [14] R. Asahi, T. Morikawa, T. Ohwaki, K. Aoki, and Y. Taga,'Visible-light photocatalysis in nitrogen-doped titanium oxides,'Science, 293, 269-271 (2001). [15] C. Giordano and M. Antonietti,'Synthesis of crystalline metal nitride and metal carbide nanostructures by sol-gel chemistry,'Nano Today, 6, 366-380 (2011). [16] S. Podsiadlo,'Stages of the synthesis of gallium nitride with the use of urea,' Thermochimica Acta, 256, 367-373 (1995). [17] S. Podsiadlo,'Stages of the synthesis of indium nitride with the use of urea,' Thermochimica Acta, 256, 375-380 (1995). [18] C. Giordano, C. Erpen, W. T. Yao, B. Milke, and M. Antonietti,'Metal nitride and metal carbide nanoparticles by a soft urea pathway,'Chemistry of Materials, 21, 5136-5144 (2009). [19] C. Giordano, C. Erpen, W. T. Yao, and M. Antoniett,'Synthesis of Mo and W carbide and nitride nanoparticles via a simple 'urea glass' route,'Nano Letters, 8, 4659-4663 (2008). [20] V. Molinari, C. Giordano, M. Antonietti, and D. Esposito'Titanium nitride-nickel nanocomposite as heterogeneous catalyst for the hydrogenolysis of aryl ethers,'Journal of the American Chemical Society, 136, 1758-1761 (2014). [21] J. J. Brancho, A. D. Proctor, S. Panuganti, and B. M. Bartlett,'Urea-glass preparation of titanium niobium nitrides and subsequent oxidation to photoactive titanium niobium oxynitrides,'Dalton Transactions, 46, 12081-12087 (2017). [22] Q. S. Gao, C. Giordano, and M. Antonietti,'Controlled synthesis of tantalum oxynitride and nitride nanoparticles,'Small, 7, 3334-3340 (2011). [23] A. Houas, H. Lachheb, M. Ksibi, E. Elaloui, C. Guillard, and J. M. Herrmann,'Photocatalytic degradation pathway of methylene blue in water,'Applied Catalysis B: Environmental, 31, 145-157 (2001). [24] L. Xiong, Y. Yang, J. X. Mai, W. L. Sun, C. Y. Zhang, D. P. Wei, Q. Chen and J. R. Ni,'Adsorption behavior of methylene blue onto titanate nanotubes,'Chemical Engineering Journal, 156, 313-320 (2010). [25] M. Gratzel,'Photoelectrochemical cells,'Nature, 414, 338-344 (2001). [26] S. L. Shinde, S. Ishii, T. D. Dao, R. P. Sugavaneshwar, T. Takei, K. K. Nanda and T. Nagao,'Enhanced solar light absorption and photoelectrochemical conversion using TiN nanoparticle-incorporated C3N4−C Dot sheets,'Applied Material and interfaces, 10, 2460-2468, (2018). [27] A. Naldoni, U. Guler, Z. X. Wang, M. Marelli, F. Malara, X. G. Meng, L. V. Besteiro, A. O. Govorov, A. V. Kildishev, A. Boltasseva and V. M. Shalaev,'Broadband hot-electron collection for solar water splitting with plasmonic titanium nitride,'Advanced Optical Materials, 5, 1601031 (2017). [28] 陳宥安,多功能氧化鐵@銀@二氧化鈦合殼複合粉體之光催化與抗菌性質研究,國立中興大學材料科學與工程學系碩士論文 (2016)。 [29] B. D. Cullity and S. R. Stock,'Elements of X-ray diffraction,'Prentice Hall, P170-171 (2001) [30] 林君緯,合殼複合氧化鐵@銀@氮摻雜二氧化鈦之染料吸附、可見光催化、磁回收與銀釋放之研究,國立中興大學材料科學與工程學系碩士論文 (2017)。 [31] M. N. Solovan, V. V. Brus, E. V. Maistruk and P. D. Maryanchuk,'Electrical and optical poperties of TiN thin films, 'Inorganic Materials, 50, 40-45 (2014). [32] M. Wittmer, B. Studer and H Melchior,'Electrical characteristics of TiN contacts to N silicon, 'Journal of Applied Physics, 52, 5722-5726 (1981). [33] J. Wang, C. M. Li, J. AO, F. Li and Z. Q. Chen,'Elastic and optical properties of IVB group transition-metal nitrides,'Acta Physica Sinica, 62, 087102 (2013).
摘要: 
本研究以尿素玻璃法製備鈦鈮氮氧複材,藉由控制尿素與金屬前驅物比值 (Urea / Metal precursor, R)調整摻氮量,探討R值對吸收光譜、能隙值及亞甲基藍染料降解等影響,並實驗決定鈦鈮氮氧複材之最佳R值。於此,吾人以尿素玻璃法製備三組條件進行比較: (1) 鈦氮氧複材、 (2) 鈦鈮氮氧複材、 (3) 以鈣離子抑制反應速率合成之鈦鈮氮氧複材。與鈦氮氧複材相比,添加鈮預計可縮減能隙值並提升染料降解效率,另外,鈦鈮氮氧複材以氯化鈣做為鈣離子抑制劑來源時,可藉由抑制尿素之碳氮鍵分離速率以達到降低團聚發生之目的,吾人並觀察氯化鈣於尿素玻璃法中扮演何種角色。
結果顯示,鈦氮氧複材與鈦鈮氮氧複材在R=1-6比較時,添加鈮之能隙值由2.75-2.45 eV縮減至2.60-2.40 eV,吸收邊界則由430-480 nm延伸至470-510 nm。吾人將鈦鈮氮氧複材之R值由1-6細分為9組,於R=3-3.5時,吸收邊界延伸至520 nm及能隙值縮減至2.40 eV,相比R=1時,其可見光光催化亞甲基藍染料降解效率由1%提升至17-19%,故R=3-3.5為具最佳光學性質之R值。至於鈣離子添加雖如預期具抑制尿素碳氮鍵分離效果,幫助降低團聚效應,但由於均勻的氨基氛圍使鈦鈮氮氧複材於R=4時僅以氮化鈦結構形成,另外,氯化鈣會以前驅物型式參與反應進而形成具鈣鈦礦結構之副產物。

In this study, Ti-Nb nitride-oxide composites were prepared by urea glass method. By controlling the ratio of urea to metal precursor (R), Ti-Nb nitride-oxide composites of different nitrogen doping levels were obtained. Absorption, band gap and organic dye photodegradation were examined in order to find the most suitable R for the Ti-Nb nitride-oxide composites. Three types of composites were prepared for comparison: (1) Ti nitride-oxide composites, (2) Ti-Nb nitride-oxide composites, and (3) Ti-Nb nitride-oxide composites with Ca-assisted preparation. The purpose was to examine whether incorporation of Nb in Ti nitride-oxide composites can obtain better optical properties and organic dye photodegradation efficiency when comparing to the Ti nitride-oxide composites. In addition, we would like to make sure whether Ca-assisted route can inhibit C-N bond release of urea and homogenize the particle-size distribution.
Our results showed that, comparing with Ti nitride-oxide composites, Ti-Nb nitride-oxide composites of different R ratios (R=1-6) reduced the band gap from 2.75-2.45 eV to 2.60-2.40 eV and had extended the absorption edge from 430-480 nm to 470-510 nm. Furthermore, it was found that Ti-Nb nitride-oxide composites of R=3-3.5 had extended the absorption edge to nearly 520 nm, and the band gap reduced to 2.40 eV. Photodegradation efficiency against methylene-blue dye increased from 1% for composites with R=1 to 17-19% for composites with R=3-3.5, that R=3-3.5 had the best optical performance. Although Ca-assisted which indicate route can homogenize particle-size, the gradually released C-N bond would let metal precursors surrounded by -NH2. This result in formation of TiN at R=4. In addition, CaCl2 facilitated formation of CaTiO3.
URI: http://hdl.handle.net/11455/97968
Rights: 同意授權瀏覽/列印電子全文服務,2019-08-23起公開。
Appears in Collections:材料科學與工程學系

Files in This Item:
File SizeFormat Existing users please Login
nchu-107-5105066020-1.pdf8.73 MBAdobe PDFThis file is only available in the university internal network   
Show full item record
 

Google ScholarTM

Check


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.