標題: Enhancing the CO2 plasticization resistance of PS mixed-matrix membrane by blunt zeolitic imidazolate framework
作者: Guo-Liang Zhuang
Hui-Hsin Tseng
Petr Uchytil
Ming-Yen Wey
關鍵字: Blunt ZIF-8;Aqueous synthetic process;CO2 capture;Plasticization;Aging
Project: Journal of CO2 Utilization, Volume 25, May 2018, Pages 79-88
A novel design to synthesize a defect-free mixed-matrix membrane (MMM) exhibiting superior gas separation performance via fully dispersed blunt zeolitic imidazolate framework (ZIF-8) in polymer matrix has been proposed for the first time. The sphericity and interconnected six-membered-ring (6-MR) pore porosity of ZIF-8 was controlled through an aqueous synthetic process by using a non-ionic surfactant (Pluronics, P123) and deionized water as solvent. The use of surfactant in ZIF-8 synthesis resulted in blunt nanocrystals with increased sphericity and 6-MR pore volume as confirmed by scanning electron microscopy (SEM) and nitrogen adsorption–desorption isotherm measurements. Subsequent pure gas permeation tests showed that blunt ZIF-8 increased CO2/N2 separation performance through “ideal morphology” in MMMs as a result of the excellent dispersion of ZIF-8 and good ZIF-8-polymer interfacial adhesion within the polymer matrix. A significant increase in CO2/N2 separation results were obtained with the MMM containing 10wt% loading of blunt ZIF-8 (P51), CO2 permeability of 21.5 Barrer (172.6%), and mixed-gas CO2/N2 selectivity of 43.9 (205.6%). The MMMs further displayed good aging-resistance properties for over 40 days, with considerable potential for long-term operation.
DOI: 10.1016/j.jcou.2018.03.009
Appears in Collections:環境工程學系所

Files in This Item:
File Description SizeFormat Existing users please Login
186.pdf2.75 MBAdobe PDFThis file is only available in the university internal network   
Show full item record

Google ScholarTM




Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.